White powder, small particle size, highly hydrophobic, high-temperature resistant, non-migrating phosphorus-based flame retardant, mainly used in engineering plastics such as polyester (PET, PBT) and nylon (PA6, PA66, PA46, including glass fiber-reinforced). Can be used alone or in synergy with nitrogen-based flame retardants for better results.
| Product | Property | Particle Size (μm) | Introduction |
| LFR-8001 | Primary Component: Diethylaluminum phosphate
Phosphorus Content: 23-24% |
<10 | Mainly used in areas with smaller particle size requirements for flame retardants such as TPE, TPU, epoxy laminated printed circuit boards. |
| LFR-8002 | Primary Component: Diethylaluminum phosphate
Phosphorus Content: 23-24% |
<10 | Primarily used in areas with ultrafine particle size requirements for powder particles, ultra-thin adhesives, flexible epoxy laminated printed circuit boards, and TPE, TPEE, PEBA. |
| LFR-8003 | Primary Component: Diethylaluminum phosphate
Phosphorus Content: 23-24% |
30-40 | Mainly used in engineering plastics of polyester and nylon (including glass fiber-reinforced and non-reinforced). |
| LFR-8005 | Primary Component: Phosphorus-nitrogen complex system
Phosphorus Content: 15-17% |
30-40 | Can be directly used in engineering plastics such as polyester (PET and PBT) and nylon 6 series, as well as TPE (TPEE, TPU, and PEBA). |
| LFR-8006 | Primary Component: Phosphorus-nitrogen complex system Phosphorus Content: 19-20% |
30-40 | Directly applicable to nylon 6 and nylon 66 series engineering plastics and TPE (TPEE, TPU, and PEBA). |
| LFR-8012 | Primary Component: Diethylaluminum phosphate Phosphorus Content: 20-21% |
<40 | High-temperature melting, conducive to melt blending with polymers, will not clog the spinnerets, suitable for PET fiber fabrics and PET film systems. Can also be used in PBT and PET injection molding. |
| LFR-5001 | Phosphorus Content > 24% | <10 | Flame retardant specifically for acrylic coating. |
| LFR-9001 | Bromine Content: 13-14%
Phosphorus Content: 6-7% |
<5 | Environmentally friendly flame retardant for PP. Low addition amount, FF-PP V2 used for homopolymer PP, adding 1% can achieve UL94 V2. |
| LFR-9002 | Bromine Content: 13-14%
Phosphorus Content: 6-7% |
<5 | Environmentally friendly flame retardant for copolymer PP. |